Umoren, S.A., State Key Laboratory for corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016, China, Department of Chemistry, Faculty of Science, University of Uyo, P.M.B 1017, Uyo, Nigeria; Li, Y., State Key Laboratory for corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016, China; Wang, F.H., State Key Laboratory for corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016, China
The corrosion behaviour of aluminium with two different microstructures namely polycrystalline (pc-Al) and microcrystalline aluminium coating (mc-Al) fabricated from the polycrystalline Al target by magnetron sputtering in 0.1M H2SO4 solution was studied. The corrosion inhibiting effect of polyacrylamide (PA) was also investigated. Results show that surface microcrystallization increases the corrosion susceptibility of aluminium leading to increase in the kinetics of the anodic dissolution. PA was found to reduce the corrosion rates of both Al samples. Inhibition efficiency of PA was concentration dependent and was more pronounced on the mc-Al specimen.